NbO2 Sintered Compact, Sputtering Target Comprising the Sintered Compact, and Method of Producing NbO2 Sintered Compact

ABSTRACT

The present invention relates to a NbO 2  sintered compact characterized in that the intensity proportion of the X-ray diffraction peak intensity of a (001) plane or (110) plane of Nb 2 O 5  relative to the X-ray diffraction peak intensity of a (400) plane of NbO 2  is 1% or less. The present invention provides, without using an expensive NbO 2  material, a NbO 2  sintered compact that can be applied to a sputtering target for forming a high-quality variable resistance layer for a ReRAM. In particular, it is an object of the present invention to provide a single phase NbO 2  sintered compact having a high density suitable for stabilizing sputtering.

TECHNICAL FIELD

The present invention relates to a niobium dioxide (NbO₂) sintered compact, a sputtering target manufactured from the sintered compact, and a method of producing a NbO₂ sintered compact.

BACKGROUND ART

In recent years, a resistive random access memory (ReRAM) has attracted attention as an alternative of flash memories. The ReRAM utilizes a large change in electric resistance by voltage application and is known to have a variable resistance layer made of an oxide of a transition metal, such as nickel, titanium, tantalum, or niobium, in particular, an oxide (suboxide) having a composition shifting stoichiometrically (see Patent Literatures 1 to 3). For example, Patent Literature 1 discloses niobium oxide (Nb₂O₅) as a variable resistance layer provided in an ReRAM.

A thin film of niobium oxide is usually formed by sputtering. For example,

Patent Literature 4, although it is an example of niobium pentoxide, discloses a sputtering target of niobium oxide produced by pressure sintering, such as hot pressing, of a niobium oxide powder.

Meanwhile, in order to most simply produce a sintered compact for a target, the composition of raw materials is adjusted to the intended composition of the sintered compact. If a raw material is expensive, even if the method is simple, the cost is increased to cause a disadvantage from the viewpoint of productivity.

Accordingly, it is known to inexpensively produce a sintered compact by reaction sintering (method of simultaneously performing synthesis and sintering) by using an inexpensive substitute for the expensive raw material. However, in production of a NbO₂ sintered compact by applying this method to an expensive material, niobium dioxide (NbO₂), for producing by reaction sintering of a Nb₂O₅ powder and a Nb powder, there occurs problems such as remaining of unreacted raw materials and formation of a large number of small pores in the sintered compact. In addition, the production of a large-sized sintered compact involves a problem of an ununiform in-plane density of the sintered compact.

Patent Literature 1: Japanese Patent Laid-Open No. 2011-149091

Patent Literature 2: Japanese Patent Laid-Open No. 2011-71380

Patent Literature 3: Japanese Patent Laid-Open No. 2007-67402

Patent Literature 4: Japanese Patent Laid-Open No. 2002-338354

SUMMARY OF INVENTION Technical Problem

The present invention provides a NbO₂ sintered compact that can be used as a sputtering target and a method of producing the NbO₂ sintered compact without using expensive NbO₂.

Solution to Problem

Accordingly, the present inventors have diligently studied for solving the above-described problems and, as a result, have found that a NbO₂ sintered compact that can be used as a sputtering target, in particular, a NbO₂ single phase sintered compact having a high density for a sputtering target, can be produced by synthesizing NbO₂ in advance from raw materials, Nb₂O₅ and Nb, and subjecting it to sintering.

On the basis of these findings, the present invention provides:

-   1) A NbO₂ sintered compact, wherein an intensity proportion of the     X-ray diffraction peak intensity of a (001) plane or (110) plane of     Nb₂O₅ relative to the X-ray diffraction peak intensity of a (400)     plane of NbO₂ is 1% or less; -   2) The NbO₂ sintered compact according to 1), wherein the intensity     proportion of the X-ray diffraction peak intensity of a (110) plane     of Nb relative to the X-ray diffraction peak intensity of a (400)     plane of NbO₂ is 1% or less; -   3) The NbO₂ sintered compact according to 1) or 2), wherein the     intensity proportion of the X-ray diffraction peak intensity of     a (400) plane of Nb₁₂O₂₉ relative to the X-ray diffraction peak     intensity of a (400) plane of NbO₂ is 5% or less; -   4) The NbO₂ sintered compact according to any one of 1) to 3),     having a relative density of 95% or more; -   5) The NbO₂ sintered compact according to any one of 1) to 4),     wherein the density variation between arbitrary points in a plane of     the sintered compact is 1.0% or less; -   6) The NbO₂ sintered compact according to any one of 1) to 5),     having a diameter of 110 mm or more; -   7) A sputtering target manufactured from the NbO₂ sintered compact     according to any one of 1) to 6); -   8) The sputtering target according to 7), having resistivity on a     surface of 100 mΩ·cm or less; -   9) The sputtering target according to 7) or 8), wherein the     sputtering target is bonded to a backing plate made of oxygen-free     copper, chromated copper, or zincated copper with an indium solder; -   10) A method of producing a NbO₂ sintered compact comprising: mixing     a Nb₂O₅ powder and a Nb powder; -   heating the resulting mixture at 1300° C. to 1400° C. in vacuum or     in an inert atmosphere to synthesize NbO₂; -   pulverizing the synthesized NbO₂; and -   sintering the pulverized powder by hot pressing at 950° C. to 1300°     C.; -   11) The method of producing a NbO₂ sintered compact according to     10), wherein the pulverized powder of the synthesized NbO₂ is     sintered by hot pressing at 950° C. to 1100° C.; -   12) The method of producing a NbO₂ sintered compact according to 10)     or 11), wherein the Nb₂O₅ powder has a purity of 99.9% or more, and     the Nb powder has a purity of 99.9% or more; and -   13) The method of producing a NbO₂ sintered compact according to any     one of 10) to 12), wherein the Nb₂O₅ powder has an orthorhombic or     monoclinic crystal system.

Advantageous Effects of Invention

According to the present invention, a NbO₂ sintered compact composed of NbO₂ synthesized from Nb₂O₅ and NbO₂ can be obtained. In particular, the present invention can provide a NbO₂ single phase sintered compact having a high density. Accordingly, the present invention has an effect that a sputtering target obtained by machining such a sintered compact does not cause abnormal discharge during sputtering to reduce occurrence of particles and achieve stable sputtering and can form a high-quality NbO₂ thin film. In addition, the present invention has an excellent effect of providing a sputtering target having a high density in response to a recent demand for large-sized sputtering targets.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a graph showing an XRD profile of NbO₂ synthesized from an orthorhombic Nb₂O₅ powder at 1300° C.

FIG. 2 is a graph showing an XRD profile of NbO₂ synthesized from a monoclinic Nb₂O₅ powder at 1300° C.

FIG. 3 is a photograph of the appearance of a sintered compact (diameter: 110 mm) of Example 2 (hot pressing at 1100° C.).

FIG. 4 is a graph showing XRD profiles of sintered compacts prepared from orthorhombic Nb₂O₅ and Nb by reaction sintering (upper stage: a sintering temperature of 1200° C., middle stage: a sintering temperature of 1100° C., lower stage: a sintering temperature of 1000° C., bottom stage: powder mixture of Nb₂O₅ and Nb).

FIG. 5 is an image of SEM observation of a sintered compact of Comparative Example 1 prepared by reaction sintering from Nb₂O₅ and Nb at 1000° C.

FIG. 6 is an image of SEM observation of a sintered compact of Comparative Example 2 prepared by reaction sintering from Nb₂O₅ and Nb at 1100° C.

FIG. 7 is an image of SEM observation of a sintered compact of Comparative Example 3 prepared by reaction sintering from Nb₂O₅ and Nb at 1200° C.

FIG. 8 is a photograph of the appearance of a sintered compact (diameter: 460 mm) of Comparative Example 4 (hot pressing at 1300° C.).

FIG. 9 is a photograph of the appearance of a sintered compact (diameter: 110 mm) of Comparative Example 5 (hot pressing at 1300° C.).

DESCRIPTION OF EMBODIMENTS

The present invention uses inexpensive materials, Nb₂O₅ and Nb, instead of the use of expensive NbO₂ and thereby can significantly reduce the manufacturing cost. The present invention can also provide a NbO₂ sintered compact having excellent characteristics that can be used in a sputtering target by being produced by synthesizing NbO₂ in advance from raw materials, Nb₂O₅ and Nb, and subjecting it to sintering.

The NbO₂ sintered compact of the present invention is substantially composed of a NbO₂ single phase. As described above, in production of a NbO₂ sintered compact from Nb₂O₅ and Nb by a common method, reaction sintering (a method simultaneously performing synthesis and sintering), complete synthesis cannot be achieved even if the conditions such as sintering temperature are controlled, and unreacted materials such as Nb₁₂O₂₉ shown in Comparative Examples below remain to form a plurality of phases in some cases. In the present invention, however, since NbO₂ is completely synthesized in advance from Nb₂O₅ and Nb and is then subjected to sintering, a sintered compact that is substantially a NbO₂ single phase can be produced. A sputtering target of such a sintered compact can stably form a NbO₂ thin film.

The NbO₂ sintered compact of the present invention is characterized in that the intensity proportion of the X-ray diffraction peak intensity of a (110) plane of Nb₂O₅ relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ is 1% or less. In addition, the intensity proportion of the X-ray diffraction peak intensity of a (110) plane of Nb is preferably 1% or less, and the intensity proportion of the X-ray diffraction peak intensity of a (400) plane of Nb₁₂O₂₉ is more preferably 5% or less. When the intensity proportions of the X-ray diffraction peak intensities of NbO₂, Nb, and Nb₁₂O₂₉ relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ are respectively 1% or less, 1% or less, and 5% or less, the sputtering target can perform stable sputtering that is substantially the same as that by a single phase NbO₂ target.

The NbO₂ sintered compact of the present invention has a high relative density of 95% or more. Accordingly, a sputtering target produced by machining the sintered compact does not cause abnormal discharge during sputtering to achieve stable sputtering and can form a high-quality thin film with reduced occurrence of particles.

In the present invention, the density variation between arbitrary points in a plane of the sintered compact can be reduced to 1.0% or less, preferably 0.5% or less, and more preferably 0.2% or less. The density variation is determined from relative densities at two arbitrary points in a plane of a sintered compact by the formula: {(higher relative density)/(lower relative density)−1}×100 (%).

Since sintering of synthesized NbO₂ by hot pressing generates a portion partially having pores, it is believed that gas occurs during the hot pressing. It is believed that this occurrence of gas causes a gentle bulge in the thickness direction from the edge to the center of the target to cause a large difference in density in a plane. In production of a large-sized sintered compact, this causes a warp or cracking in the sintered compact. Therefore, the present invention is particularly effective in production of a large-sized sintered compact.

The present invention exhibits an excellent effect on, in particular, a large-sized NbO₂ sintered compact having a diameter of 110 mm or more, furthermore, a diameter of 460 mm or more. As described above, in production of a large-sized sintered compact, there is a risk of causing a change in the shape of the sintered compact, unlike production of a small-sized sintered compact. That is, in a sintered compact having a diameter of smaller than 110 mm, conditions set for hot pressing of a small-sized sample can be directly applied to production of the sintered compact. However, in a sintered compact having a diameter of 110 mm or more, if the conditions for hot pressing determined using a small-sized sample are directly applied to production of the sintered compact, changes in, for example, the shape of the sintered compact occur, resulting in a difficulty in producing a sintered compact having a high density. However, the sintered compact of the present invention does not have an upper limit in size, and from the viewpoint of manufacturing, a diameter up to about 480 mm is preferred.

The NbO₂ sintered compact of the present invention can be produced by, for example, as follows. The present invention is characterized in that since a commercially available NbO₂ powder is expensive and takes a lot of time to obtain, inexpensive Nb₂O₅ powder and Nb powder are used.

First, an orthorhombic or monoclinic crystal Nb₂O₅ powder having a purity of 99.9% and a Nb powder having a purity of 99.9% are prepared. These powders are mixed and are then subjected to heat treatment for synthesis. The temperature of the heat treatment can be appropriately determined while confirming the state of the synthesis and is preferably 1200° C. to 1400° C. in vacuum or in an inert atmosphere. A heat treatment at lower than 1200° C. disadvantageously causes remaining of Nb and synthetic intermediates due to, for example, insufficient mixing. The temperature of the heat treatment is preferably higher than 1200° C., more preferably higher than 1300° C., and is preferably 1400° C. or lower from the viewpoint of the facilities and productivity.

Subsequently, the synthesized NbO₂ powder is sintered by hot pressing. The synthesized NbO₂ powder is coarse and is pulverized before sintering. The pulverization can be performed by a known method. For example, a jet mill or SC mill can be used, and the grain size after pulverization is preferably 0.1 to 10.0 μm.

On this occasion, the hot-pressing sintering temperature is adjusted to 950° C. to 1300° C. Generally, a higher temperature tends to increase the relative density. In the case of the NbO₂ powder, however, since a sintering temperature of higher than 1300° C. may cause cracking in the sintered compact due to the emission gas during the sintering, the upper limit of the sintering temperature is 1300° C. The lower limit of the sintering temperature is 950° C., because thermomechanical analysis (TMA) demonstrates that a temperature of 950° C. or lower cannot provide monotonous contraction.

In a case of a large-sized sintered compact, in particular, in a case of a sintered compact having a diameter of 110 mm or more, the hot-pressing sintering temperature is preferably 950° C. to 1100° C. If the sintering temperature is higher than 1100° C., the emission gas during the sintering reduces the density of the sintered compact and generates a difference in the density between an arbitrary point in the periphery (within 30 mm from the edge) and the central portion in a plane of the sintered compact, and may also cause cracking in the sintered compact itself.

Thus, a single phase NbO₂ sintered compact having a relative density of 95% or more can be produced. This sintered compact can be produced into a sputtering target by machining such as cutting and polishing.

EXAMPLES

The present invention will now be described by Examples and Comparative Examples. The Examples are merely exemplary and are not intended to limit the scope of the present invention. That is, the present invention is limited only by the claims and encompasses various modifications in addition to the Examples included in the present invention.

Example 1

An orthorhombic Nb₂O₅ powder having a purity of 99.9% and a Nb powder having a purity of 99.9% were mixed. The mixture was placed in a carbon crucible and was heated in an inert gas atmosphere. The heat treatment temperature was 1300° C., and the treatment time was 2 hours. The crystal structure of the Nb₂O₅ powder is not influenced by the heat treatment results, and the heat treatment time depends on the throughput and the structure of the furnace and is not limited to the above. FIG. 1 shows the result of X-ray diffraction analysis after the heat treatment synthesis. The intensity proportion of the X-ray diffraction peak intensity of a (400) plane of Nb₁₂O₂₉ appearing on the way of synthesis relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ was 1.7%; the intensity proportion of the X-ray diffraction peak intensity of a (001) plane of Nb₂O₅ relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ was 0.1% or less; and the intensity proportion of the X-ray diffraction peak intensity of a (110) plane of Nb relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ was 0.1%. The amount of Nb in the synthesized material measured by ICP was 74.5 wt %, against the theoretical value of 74.4 wt %, to demonstrate that NbO₂ was synthesized.

Subsequently, the synthesized NbO₂ powder was sintered by hot pressing. Since aggregation occurs during the synthesis, the powder at this point has a coarse grain size. Accordingly, the powder was pulverized with a jet mill to give a grain diameter of about 1.4 μm. The hot-pressing sintering was performed at a hot-pressing temperature of 1100° C. to provide an intended shape having a diameter of 30 mm and a thickness of 9 mm. As a result, the average relative density value was high, 96.9%. The relative density was calculated on the basis of a true density (theoretical density) of 5.9 g/cm³. Since the diameter of this sintered compact was small, 30 mm, verification of the in-plane density distribution is useless and was not performed. Table 1 shows the results.

TABLE 1 Ratio (%) to XRD NbO₂ (400) Synthesis Nb₂O₅ (001) Nb₂O₅ Nb Temp. Time or powder powder Existence (° C.) (hr) Nb (100) Nb₂O₅ (110) Nb₁₂O₂₉ Example 1 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% 2 monoclinic 99.9% Yes 1300 2 0.3 ≦0.1 4.6 99.9% 3 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% 4 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% 5 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% 6 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% 7 monoclinic 99.9% Yes 1300 2 0.4 ≦0.1 4.6 99.9% Comparative 1 orthorhombic 99.9% No — — 25.2 0.5 38.0 Example 99.9% 2 orthorhombic 99.9% No — — 8.0 0.5 14.5 99.9% 3 orthorhombic 99.9% No — — 0.8 0.1 3.9 99.9% 4 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% 5 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% 6 orthorhombic 99.9% Yes 1300 2 0.1 ≦0.1 1.7 99.9% Hot press Density Resistivity Diameter Temp. Density Distribution on a surface (mm) (° C.) (%) (%) mΩ · cm Note Example 1 30 1100 96.9 — — 2 30 1050 96.5 — — 3 110 1100 95.8 ≦0.2 37.7  Used the powder synthesized in Example 1 4 110 950 96.6 ≦0.2 1.5 Used the powder synthesized in Example 1 5 460 1060 97.1 ≦0.5 2.1 Used the powder synthesized in Example 1 6 460 950 95.2 ≦0.5 — Used the powder synthesized in Example 1 7 460 1050 96.6 — 2.5 Used the powder synthesized in Example 2 Comparative 1 30 1000 — — — Example 2 30 1100 — — — 3 30 1200 — — — 4 110 1300 85.0 6.1 — Used the powder synthesized in Example 1 5 460 1300 79.5 3.1 — Used the powder synthesized in Example 1 6 110 900 88.6 0.9 — Used the powder synthesized in Example 1

Example 2

A monoclinic Nb₂O₅ powder having a purity of 99.9% and a Nb powder having a purity of 99.9% were mixed. The mixture was placed in a carbon crucible and was heated in vacuum. The heat treatment temperature was 1300° C., and the treatment time was 2 hours. The crystal structure of the Nb₂O₅ powder is not influenced by the heat treatment results, and the heat treatment time depends on the throughput and the structure of the furnace and is not limited to the above. FIG. 2 shows the result of X-ray diffraction analysis after the heat treatment synthesis. The intensity proportion of the X-ray diffraction peak intensity of a (400) plane of Nb₁₂O₂₉ appearing on the way of synthesis relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ was 4.6%; the intensity proportion of the X-ray diffraction peak intensity of a (001) plane of Nb₂O₅ relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ was 0.1% or less; and the intensity proportion of the X-ray diffraction peak intensity of a (110) plane of Nb relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ was 0.3%. The amount of Nb in the synthesized material measured by ICP was 74.0 wt %, against the theoretical value of 74.4 wt %, to demonstrate that NbO₂ was synthesized.

Subsequently, the synthesized NbO₂ powder was sintered by hot pressing. Since aggregation occurs during the synthesis, the powder at this point has a coarse grain size. Accordingly, the powder was pulverized with a jet mill to give a grain diameter of about 1.4 μm. The hot-pressing sintering was performed at a hot-pressing temperature of 1050° C. to provide an intended shape having a diameter of 30 mm and a thickness of 9 mm. As a result, the average relative density value was high, 96.5%. The relative density was calculated on the basis of a true density (theoretical density) of 5.9 g/cm³. Since the diameter of this sintered compact was small, 30 mm, verification of the in-plane density distribution is useless and was not performed.

Example 3

The pulverized NbO₂ powder obtained in Example 1 was sintered by hot pressing at 1100° C. to produce a sintered compact having a diameter of 110 mm. As a result, the average relative density value of the resulting sintered compact was high, 95.8%, to suppress the density variation in in-plane distribution to 0.2% or less. As shown in FIG. 2, no specific abnormality was observed in the appearance of the sintered compact. Furthermore, the surface of the sintered compact was ground, and the resistivity on a surface was measured by a four-terminal method and was found to be 37.7 mΩ·cm.

Example 4

The pulverized NbO₂ powder obtained in Example 1 was sintered by hot pressing at 950° C. to produce a sintered compact having a diameter of 110 mm.

As a result, the average relative density value of the resulting sintered compact was high, 96.6%, to suppress the density variation in in-plane distribution to 0.2% or less. Although it is not shown in drawings, no specific abnormality was observed in the appearance of the sintered compact. Furthermore, the surface of the sintered compact was ground, and the resistivity on a surface was measured by a four-terminal method and was found to be 1.5 mΩ·cm. Thus, favorable electrical conductivity was obtained.

Example 5

The pulverized NbO₂ powder obtained in Example 1 was sintered by hot pressing at 1060° C. to produce a sintered compact having a diameter of 460 mm. As a result, the average relative density value of the resulting sintered compact was high, 97.1%, to suppress the density variation in in-plane distribution to 0.5% or less. Although it is not shown in drawings, no specific abnormality was observed in the appearance of the sintered compact. Furthermore, the surface of the sintered compact was ground, and the resistivity on a surface was measured by a four-terminal method and was found to be 2.1 mΩ·cm. Thus, favorable electrical conductivity was obtained.

Example 6

The pulverized NbO₂ powder obtained in Example 1 was sintered by hot pressing at 950° C. to produce a sintered compact having a diameter of 460 mm. As a result, the average relative density value of the resulting sintered compact was high, 95.2%, to suppress the density variation in in-plane distribution to 0.5% or less. Although it is not shown in drawings, no specific abnormality was observed in the appearance of the sintered compact.

Example 7

The pulverized NbO₂ powder obtained in Example 2 was sintered by hot pressing at 1050° C. to produce a sintered compact having a diameter of 460 mm. As a result, the average relative density value of the resulting sintered compact was high, 96.6%. Since the measurement of in-plane density distribution is a destructive test, this sintered compact was not evaluated. However, from the results in Examples 3, 4, 5, and 6, the in-plane distribution can be expected to have a density variation of 0.5% or less. Subsequently, this sintered compact was processed into a disk shape having a diameter of 425 mm and a thickness of 6.35 mm. It was further bonded to a backing plate made of oxygen-free copper with indium (In) solder. The resistivity of the NbO₂ surface was measured by a four-terminal method and was found to be 2.5 mΩ·cm. Thus, favorable electrical conductivity was obtained.

Comparative Example 1

A Nb₂O₅ powder having a purity of 99.9% and a Nb powder having a purity of 99.9% were mixed. The mixture was subjected to reaction sintering that simultaneously performs synthesis and sintering. The reaction sintering was performed using a hot press at a hot-pressing temperature of 1000° C. to give a diameter of 30 mm and a thickness of 9 mm.

FIG. 4 shows a microscopic photograph of the surface of the resulting sintered compact. The result demonstrated that materials (light gray portion) other than NbO₂ remained. The surface of the sintered compact was inspected by X-ray diffraction analysis. As a result, as shown in the lower stage of FIG. 3, peaks of Nb, Nb₁₂O₂₉ as an intermediate during the synthesis, and so on were observed. Thus, the synthesis of NbO₂ was incomplete in Comparative Example 1.

Comparative Example 2

A sintered compact was produced by reaction sintering as in Comparative Example 1 except that the hot-pressing temperature was 1100° C. FIG. 5 shows a microscopic photograph of the surface of the resulting sintered compact. The result demonstrated that materials (light gray portion) other than NbO₂ remained and that pores were formed in the periphery of the metal Nb. The surface of the sintered compact was inspected by X-ray diffraction analysis. As a result, as shown in the middle stage of FIG. 3, peaks of Nb, Nb₁₂O₂₉ as an intermediate during the synthesis, and so on were observed. Thus, the synthesis of NbO₂ was incomplete in Comparative Example 2.

Comparative Example 3

A sintered compact was produced as in Comparative Example 1 except that the hot-pressing temperature was 1200° C. FIG. 6 shows a microscopic photograph of the surface of the resulting sintered compact. The result demonstrated that a large number of pores were formed in the periphery of the metal Nb. The surface of the sintered compact was inspected by X-ray diffraction analysis. As a result, as shown in the upper stage of FIG. 3, peaks of Nb, Nb₁₂O₂₉ as an intermediate during the synthesis, and so on were observed. Thus, the synthesis of NbO₂ was incomplete in Comparative Example 3.

Comparative Example 4

The pulverized NbO₂ powder obtained in Example 1 was sintered by hot pressing at 1300° C. to produce a sintered compact having a diameter of 110 mm. As a result, the average relative density value of the resulting sintered compact was significantly low, 85.0%, and the density variation in in-plane distribution was deteriorated to 6.1%. In addition, as shown in FIG. 7, the central portion was cracked to form a depression observed in the appearance of the sintered compact. This cracking is believed to be caused by occurrence of gas (emission gas) during the sintering.

Comparative Example 5

The pulverized NbO₂ powder obtained in Example 1 was sintered by hot pressing at 1300° C. to produce a sintered compact having a diameter of 460 mm. As a result, the average relative density value of the resulting sintered compact was significantly low, 79.5%, and the density variation in in-plane distribution was deteriorated to 3.1%. In addition, as shown in FIG. 8, the central portion was cracked to form a depression observed in the appearance of the sintered compact. This cracking is believed to be caused by occurrence of gas (emission gas) during the sintering.

Comparative Example 6

The pulverized NbO₂ powder obtained in Example 1 was sintered by hot pressing at 900° C. to produce a sintered compact having a diameter of 110 mm. As a result, though the density variation in in-plane distribution of the resulting sintered compact was low, 0.9%, the average relative density value was significantly low, 88.6%. Thus, when the hot-pressing temperature was low, though there was no problem in the in-plane density distribution, the density was low, resulting in insufficient sintering.

INDUSTRIAL APPLICABILITY

The NbO₂ sintered compact of the present invention can be used in a sputtering target. The thin film formed using this sputtering target is useful as a high-quality variable resitance layer that is used in a ReRAM. Another notable characteristic of the present invention is that a single phase Nb0₂ sintered compact having a high density can be obtained without using any expensive material, which allows stable sputtering and is very useful for the promotion of production efficiency in recent years. 

1. A NbO₂ sintered compact sputtering target, wherein an intensity proportion of the X-ray diffraction peak intensity of a (001) plane or (110) plane of Nb2O₅ relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ is 1% or less, and a relative density is 95% or more.
 2. The NbO₂ sintered compact sputtering target according to claim 1, wherein the intensity proportion of the X-ray diffraction peak intensity of a (110) plane of Nb relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ is 1% or less.
 3. The NbO₂ sintered compact sputtering target according to claim 1 or claim 2, wherein the intensity proportion of the X-ray diffraction peak intensity of a (400) plane of Nb₁₂O₂₉ relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ is 5% or less.
 4. (canceled)
 5. The NbO₂ sintered compact sputtering target according claim 3, wherein the density variation between arbitrary two points in a plane of the sintered compact sputtering target is 1.0% or less.
 6. The NbO₂ sintered compact sputtering target according to claim 5, having a diameter of 110 mm or more.
 7. (canceled)
 8. The sputtering target according to claim 6, having resistivity on a surface of 100 mΩ·cm or less.
 9. The sputtering target according to claim 8, wherein the sputtering target is bonded to a backing plate made of oxygen-free copper, chromated copper, or zincated copper with an indium solder.
 10. A method of producing a NbO₂ sintered compact, comprising: mixing a Nb₂O₅ powder and a Nb powder; heating the resulting mixture at 1300° C. to 1400° C. in vacuum or in an inert atmosphere to synthesize NbO₂; pulverizing the synthesized NbO₂; and sintering the pulverized powder by hot pressing at 950° C. to less than 1300° C.
 11. The method of producing a NbO₂ sintered compact according to claim 10, wherein the pulverized powder of the synthesized NbO₂ is sintered by hot pressing at 950° C. to 1100° C.
 12. The method of producing a NbO₂ sintered compact according to claim 11, wherein the Nb₂O₅ powder has a purity of 99.9% or more, and the Nb powder has a purity of 99.9% or more.
 13. The method of producing a NbO₂ sintered compact according to claim 12, wherein the Nb₂O₅ powder has an orthorhombic or monoclinic crystal system.
 14. The method of producing a NbO₂ sintered compact according to claim 10, wherein the Nb₂O₅ powder has a purity of 99.9% or more, and the Nb powder has a purity of 99.9% or more.
 15. The method of producing a NbO₂ sintered compact according to claim 10, wherein the Nb₂O₅ powder has an orthorhombic or monoclinic crystal system.
 16. The NbO₂ sintered compact sputtering target according to claim 1, wherein the intensity proportion of the X-ray diffraction peak intensity of a (400) plane of Nb₁₂O₂₉ relative to the X-ray diffraction peak intensity of a (400) plane of NbO₂ is 5% or less.
 17. The NbO₂ sintered compact sputtering target according to claim 1, wherein the density variation between arbitrary two points in a plane of the sintered compact sputtering target is 1.0% or less.
 18. The NbO₂ sintered compact sputtering target according to claim 1, having a diameter of 110 mm or more.
 19. The sputtering target according to claim 18, having resistivity on a surface of 100 mΩ·cm or less.
 20. The sputtering target according to claim 19, wherein the sputtering target is bonded to a backing plate made of oxygen-free copper, chromated copper, or zincated copper with an indium solder. 